Technical parameters 

 Project 
 Units 
 Indicators 

 Bending strength 
 Mpa 
 ≥ 200 

 Compressive strength 
 Mpa 
 ≥ 150 

 Impact strength 
 J / cm 2 
 ≥ 150 

 40% sulfuric acid 
 / 
 No change in 20 days 

 30% sodium hydroxide 
 / 
 No change in 20 days 

 20% hydrochloric acid 
 / 
 No change in 20 days 

 95% ethanol 
 / 
 No change for 30 days 




 Features 

 Dust, corrosion, high hardness, resistance to severe impact, abrasion, oil resistant, waterproof, no distortion, easy to clean, and bright and clean, bright. 

 Construction steps 

 1, Su deal: First of all elements with the mill carried out on polished, uneven office is required to grind, and wet cleaning the place dry and clean, to reach the smooth, clean, no loose, no oil, dry (moisture ≤ 8 %). 

 2, primer: in the resin by adding a certain percentage of the adhesive agent and penetrating agent, then coated with a good resin pigment ground in dealing with good, the resin to penetrate into the internal factors, such reinforcement can play fill the pores and The role of the foundation. 

 3, quartz sand: to be cured primer, then a certain percentage of resin added aggregate and mix well. Evenly with a trowel in the primer on the grant. After curing can increase the flatness of the floor, you can also play a resistant to pressure, impact resistance, and so on. 

 4, batch coating: to be cured of quartz sand, with its grinding mill, and then clean up, and then aggregate at a certain percentage of resin added Stir approved by trowel evenly on the quartz sand in Deal . 

 5, top coat: in the first cured coating were polished, then clean up, and then MT-303 resin by adding a certain color paste to do top coat. Topcoat for the self-leveling, covering power of good, and coloring free, clean and bright, nice.